CORROSION OF THE REINFORCED CONCRETE IN THE BUILDING FOR ELECTROLYTE PREPARATION FOR BATTERY INDUSTRY TREPÇA

SADIKU, ALI; RAMA, MURSEL; SHALA, FERAT; SKEJA, BEHAJDIN; BAJRAKTARI, BEKIM; SADIKU, MILAIM

AKTET - Journal of Institute Alb-Shkenca
AKTET, Volume 4, Issue 2, Gjeologji, Metalurgji, Inxhinieri Kimike, Riciklim, 2011

Title: CORROSION OF THE REINFORCED CONCRETE IN THE BUILDING FOR ELECTROLYTE PREPARATION FOR BATTERY INDUSTRY TREPÇA

Titulli shqip: KORROZIONI I BETONARMESË NË OBJEKTIN PËR PËRGATITJEN E ELEKTROLITIT NË INDUSTRINË E BATERIVE TREPÇA

Abstract: Constructions which are built from reinforced concrete during their utilization are exposed to harmful agents, which can be of chemical or physical nature. On the premises of electrolytes preparation in Battery Factory Trepça are clearly notice the impact of aggressive environment in concrete. Surface area of the building was protected with acid resistant ceramics, but corrosion is noticeable across most of the surface, manifested as sulphate type corrosion. Corrosion products are sulphate salts that have large volume and cause separation between protective layer and concrete and damage the structure of reinforced concrete. The formation of cracks creates the conditions for corrosion of steel bars, which is the electrochemical process that has consequences on the functionality and security of the facility. The purpose of the paper is to determine the degree of damage, consequences of degradation of concrete and measures to be taken for protection from further corrosion at the facility.

Abstrakti: Konstruksionet e objekteve të cilat janë nga betonarmeja gjatë shfrytëzimit i nënshtrohen veprimit të dëmshëm të faktorëve të natyrës kimike dhe fizike. Në objektin për përgatitjen e elektrolitit në Ind. e baterive Trepça, vërehet shumë qartë ndikimi i mesit agresiv në korrozionin e betonit. Sipërfaqja e ndërtesës ka qenë e mbrojtur me pllaka kundër acide, por korrozioni ka përfshirë shumicën e sipërfaqes dhe është korrozion sulfat. Produktet e korrozionit janë kripëra sulfat që kanë vëllim të madh dhe shkaktojne ndarje në mes shtresës mbrojtëse e betonit dhe dëmtim të strukturës së betonarmesë. Me formimin e plasaritjeve krijohen kushte që të korrodojnë shufrat e çelikut në beton, qe është proces elektrokimik e që ka pasoja në funksionalitetin dhe sigurinë e objektit. Qëllimi i punimit është përcaktimi i shkallës së dëmtimit, pasojat nga degradimi i betonit dhe masat që duhet ndërmarr për mbrojtjen nga korrozioni i mëtejme në objekt.

Key words: sulfuric acid, concrete, reinforced concrete, steel, corrosion.

Fjalë kyçe: acid sulfurik, beton, betonarme, çelik, korrozion

Corresponding author: ALI SADIKU (alisadiku@hotmail.com)

Authors: ALI SADIKU, FXM, Mitrovicë, Kosova
MURSEL RAMA, FXM, Mitrovicë, Kosova
FERAT SHALA, FIM, Prishtinë, Kosova
BEHAJDIN SKEJA, FXM, Prizren, Kosova
BEKIM BAJRAKTARI, FSHTA Mitrovicë, Mitrovicë, Kosova
MILAIM SADIKU, FXM, Mitrovicë, Kosova

Full text: Download Issue 2 [PDF]

	AKTET Journal of Institute Alb-Shkenca Revistë Shkencore e Institutit Alb-Shkenca ( ISSN 2073-2244 )
(english)

Title:	CORROSION OF THE REINFORCED CONCRETE IN THE BUILDING FOR ELECTROLYTE PREPARATION FOR BATTERY INDUSTRY TREPÇA
Titulli shqip:	KORROZIONI I BETONARMESË NË OBJEKTIN PËR PËRGATITJEN E ELEKTROLITIT NË INDUSTRINË E BATERIVE TREPÇA
Abstract:	Constructions which are built from reinforced concrete during their utilization are exposed to harmful agents, which can be of chemical or physical nature. On the premises of electrolytes preparation in Battery Factory Trepça are clearly notice the impact of aggressive environment in concrete. Surface area of the building was protected with acid resistant ceramics, but corrosion is noticeable across most of the surface, manifested as sulphate type corrosion. Corrosion products are sulphate salts that have large volume and cause separation between protective layer and concrete and damage the structure of reinforced concrete. The formation of cracks creates the conditions for corrosion of steel bars, which is the electrochemical process that has consequences on the functionality and security of the facility. The purpose of the paper is to determine the degree of damage, consequences of degradation of concrete and measures to be taken for protection from further corrosion at the facility.
Abstrakti:	Konstruksionet e objekteve të cilat janë nga betonarmeja gjatë shfrytëzimit i nënshtrohen veprimit të dëmshëm të faktorëve të natyrës kimike dhe fizike. Në objektin për përgatitjen e elektrolitit në Ind. e baterive Trepça, vërehet shumë qartë ndikimi i mesit agresiv në korrozionin e betonit. Sipërfaqja e ndërtesës ka qenë e mbrojtur me pllaka kundër acide, por korrozioni ka përfshirë shumicën e sipërfaqes dhe është korrozion sulfat. Produktet e korrozionit janë kripëra sulfat që kanë vëllim të madh dhe shkaktojne ndarje në mes shtresës mbrojtëse e betonit dhe dëmtim të strukturës së betonarmesë. Me formimin e plasaritjeve krijohen kushte që të korrodojnë shufrat e çelikut në beton, qe është proces elektrokimik e që ka pasoja në funksionalitetin dhe sigurinë e objektit. Qëllimi i punimit është përcaktimi i shkallës së dëmtimit, pasojat nga degradimi i betonit dhe masat që duhet ndërmarr për mbrojtjen nga korrozioni i mëtejme në objekt.
Key words:	sulfuric acid, concrete, reinforced concrete, steel, corrosion.
Fjalë kyçe:	acid sulfurik, beton, betonarme, çelik, korrozion
Corresponding author:	ALI SADIKU (alisadiku@hotmail.com)
Authors:	ALI SADIKU, FXM, Mitrovicë, Kosova MURSEL RAMA, FXM, Mitrovicë, Kosova FERAT SHALA, FIM, Prishtinë, Kosova BEHAJDIN SKEJA, FXM, Prizren, Kosova BEKIM BAJRAKTARI, FSHTA Mitrovicë, Mitrovicë, Kosova MILAIM SADIKU, FXM, Mitrovicë, Kosova
Full text:	Download Issue 2 [PDF]